Drizoro - Maxepox Elastic epoxy resin
Price on request
Product description
Two-component, flexible epoxy resin, especially for sealing joints and cracks and creating a flexible surface mortar and elastic coating on concrete floors.
Features
- resistance to a wide range of temperatures from -30 C to +80 C
- good fluidity - the product can be applied by pouring
- high flexibility and ability to carry cracks - up to 1.25 mm
- very good resistance to many different compounds and chemicals: oils, fats, gasoline, acid and alkaline solutions, solvents, salts, etc.
- excellent adhesion to concrete, cement mortar, steel, wood, aluminum, glass, etc.
- waterproofing properties
- favorable proportion of resin in relation to sand - the possibility of saving costs in the case of filling and anchoring works
- non-toxic
- solvent-free
- non-flammable
- suitable for use in places with poor ventilation
- consisting of 100% constants
Application
- flexible sealing and creating a crack-bridging coating on very cracked floors
- sealing and flexible filling of joints on floors
- as a primer and base coat in floor systems exposed to thermal movements, vibrations and a high risk of cracks
- creating a flexible mortar containing silicate sand and coatings with the possibility of high movement transmission, filling or grouting places for machines and devices, etc.
- fixing and filling in tram tracks
Technical data
- external appearance and color component in A and B: transparent liquid
- A: B component weight ratio in the mixture of 1.35: 1
- element content in solids in the mixture A + B 100%
- specific gravity of A + B mixture 1.02 0.1 g / cm 3
- flash point - non-flammable material
- minimum substrate and ambient temperature> 10 ° C
- shelf life of the A + B mix at 10 C / 20 C / 30 C 60/45/30 min
- touch-drying time of the A + B mixture at 10 C / 20 C / 30 C 24/18/8 h
- time from product application to application of the next layer at a temperature of 20 C 24 h
- maturing time at 20 ° C 48 h
- tensile strength / elongation at 20 C 0.4 MPa / 190%
- tensile strength / elongation at -10 C 1.20 MPa / 75%
- Shore hardness 45 (according to ISO 868)
- crack transmission capacity according to EN 1062-7: 2004 - width of the transferred crack 1.25 mm; class: A4
- consumption: as a base 0.4–0.5 kg / m 2 ; as a flexible coating one layer / total 0.4-0.5 / 0.8-1.0 kg / m 2 ; as a flexible grout at the joint 1.05-1.15 kg / l