Air-oxygen-curing 3-20 mm joint mortar, based on synthetic resin, for lightly loaded paving, ceramic and stone coverings, especially for porcelain stoneware tiles with a thickness of ≥ 2 cm on a set and unbound substructure.
Features
- one-component
- ready to use
- optimal water permeability
- possibility of building in during light rainfall
- resistant to mr z / sl used for deicing
- for joint widths from 3 mm
- slime consistency, easy to apply
- drainage properties
- provides a uniform appearance to the cladding
- no lichen in the plant
- waterproof
- frost-resistant
- outside
Application
- grouting paving, natural stone, ceramic, clinker cladding, and especially porcelain terrace tiles with a thickness of ≥ 2 cm in external areas on a bound and unbound substructure
- pointing of untreated, high-quality concrete slabs
- for applications in lightly loaded areas, such as building entrance areas, terraces, paths and garden areas
Technical data
- mixing ratio ready to use
- application time approx. 45 minutes at +20 ° C
- can be walked on after about 24 hours at a temperature of +20 C (protect the freshly grouted surface)
- fully loaded after about 7 days
- bending strength of about 6 N / mm 2
- compressive strength approx. 15 N / mm 2
- water permeability 1.7 x 10 -5 m / s (with a 5% share of the grout about 3 l / m 2 / h)
- joint width / depth from 3 mm to a maximum of 20 mm / at least 30 mm (for paving stones); from 15 mm / at least double the joint width; the depth of the joint when replacing the joints of the paving stone, minimum 2/3 of the height of the stone
- application temperature from +3 C to +25 C.
- consumption from 0.6 kg / m 2 to 27.9 kg / m 2
- 18-month storage
- package 25 kg