A flexible, one-component, polyurethane based sealant that matures on contact with ambient moisture. By applying this material, we obtain a strong and very elastic seal in a wide temperature range.
Features
- ready-to-use sealant; does not require additional mixing on site
- it has excellent adhesion to construction materials such as concrete and brick; natural stone; glass; wood; steel; metal
Application
Used to fill expansion joints with certain movements, construction joints, wherever permanent elastic filling is required, e.g .:
- as a filling material for expansion joints in floors
- as a filling material for dilatations in water reservoirs and sewage treatment plants wastewater in - in connections element in prefabricated (large slab)
- for sealing doors and windows
- in sealing roof panels
- when sealing the balcony and terrace in
Technical data
- density 1.3 g / cm 3
- application and maturation temperature + 5 ° C to + 40 ° C
- film formation at 23 C and 50% humidity 60-100 min
- hardening for 24 h at 23 C and 50% relative humidity 3 mm
- movement of expansion joints during use 25%
- tensile strength 0.40 MPa
- 100% elongation tensile strength (MPa) 0.46 MPa
- elongation at break 80%
- compressibility 80%
- Shore A hardness 40
- temperature range during use from 20 C to + 80 C
- resistance to action: aqueous solution with SO 4 ion content from 2 to 6000 mg / l '; an aqueous solution with an ion content in NH 4 + up to 100 mg / l; an aqueous solution with an ion content in Mg2 + up to 3000 mg / l; aqueous solution in hydrochloric acid at a concentration of up to 1%; aqueous phenol solution up to a concentration of 1%; Kit Maxflex 100 LM is resistant to the occasional effect of an aqueous solution in sodium hypochlorite with a concentration of up to 1%
- consumption - 100 ml is needed to fill 1 running meter of a 10x10 mm joint
- package: sausage 0.6 l, carton of 20 pieces