Drizoro - Maxepox Morter epoxy binder

Two-component, chemically hardening binder based on epoxy resins. After mixing with a suitable aggregate, e.g. quartz sand, it is possible to obtain a covering material as well as a mortar with high mechanical and chemical resistance and an aesthetic appearance.

Features

• abrasion resistant
• decorative, available in many colors
• when using a transparent variety, colored aggregates can be used
• the possibility of making a smooth or anti-slip surface of the expedition
• high chemical and mechanical resistance
• easy to keep clean

Application

• floor coverings of concrete slabs in garages, wholesalers, sports centers, etc.
• insulation and surface on communication facilities such as bridges, viaducts, tunnels
• as a multilayer coating with sand sprinkles - on concrete substrates that may be loaded with pedestrians, cyclists and light vehicular traffic,
• as a mortar - on concrete substrates for which loads corresponding to the harsh conditions of road transport are expected - vehicles on steel wheels with an axle load exceeding 6 kN or on pneumatic wheels with an axle load exceeding 50 kN
• as a coating protection for concrete surfaces with a slight slope

Technical data

• color and appearance of component B yellow liquid
• Component ratios in epoxy A: B 2.33: 1 kg
• proportion - binder: aggregate (maximum / minimum) for 1: 5/1: 6 mortar
• solids 100%
• mortar density 2.1 g / cm ³
• service life 10 C / 20 C / 30 C - 120/80/40 min
• hardening time 10 C / 20 C / 30 C 24/18/8 h
• commissioning period 3 days
• compressive strength of the mortar 80.0 MPa
• bending strength of the mortar 25.0 MPa
• modulus of elasticity 12,500 MPa
• linear expansion coefficient 20 x 10 ^-6 1 / C
• consumption / thickness as epoxy based mortar 2,1; wear as a 0.5 epoxy based coating; recommended thickness for epoxy based mortar 4-5
• 10 kg and 20 kg packaging